难熔金属
外观
![本页使用了标题或全文手工转换](http://upload.wikimedia.org/wikipedia/commons/thumb/c/cd/Zh_conversion_icon_m.svg/35px-Zh_conversion_icon_m.svg.png)
H | He | ||||||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Li | Be | B | C | N | O | F | Ne | ||||||||||||
Na | Mg | Al | Si | P | S | Cl | Ar | ||||||||||||
K | Ca | Sc | Ti | V | Cr | Mn | Fe | Co | Ni | Cu | Zn | Ga | Ge | As | Se | Br | Kr | ||
Rb | Sr | Y | Zr | Nb | Mo | Tc | Ru | Rh | Pd | Ag | Cd | In | Sn | Sb | Te | I | Xe | ||
Cs | Ba | * | Lu | Hf | Ta | W | Re | Os | Ir | Pt | Au | Hg | Tl | Pb | Bi | Po | At | Rn | |
Fr | Ra | ** | Lr | Rf | Db | Sg | Bh | Hs | Mt | Ds | Rg | Cn | Nh | Fl | Mc | Lv | Ts | Og | |
* | La | Ce | Pr | Nd | Pm | Sm | Eu | Gd | Tb | Dy | Ho | Er | Tm | Yb | |||||
** | Ac | Th | Pa | U | Np | Pu | Am | Cm | Bk | Cf | Es | Fm | Md | No | |||||
难熔金属
| |||||||||||||||||||
广义的难熔金属[1]
|
难熔金属(英语:Refractory metals),又称耐火金属、耐高温金属、高熔点金属,是指特别耐热不易熔化,并且具有耐磨性的金属。此术语主要是用在材料科学、和冶金工程。这些元素在不同领域中的的定义方式有些不同。最常见的定义方式包括五个元素:两个第五周期元素(铌、钼)和三个第六周期元素(钽、钨、铼)。这些元素有一些共同性质,包括熔点超过2000 °C以上,在室温下具很高的硬度。由于其化学惰性,不易与其他元素反应,而其密度也相对较高。难熔金属因为高熔点,是粉末冶金方法制造的首选。难熔金属的一些应用包括金属工具,高温工作、丝纤维、铸造模具,或在腐蚀性环境中的化学反应器。部分是由于熔点高,难熔金属在很高温下,也不会有蠕变变形的情形。
定义
[编辑]在大多数定义下,只有具有极高熔点的金属元素才会列入难熔金属。根据一项定义,熔点超过4000°F(2200 °C)是必须条件。[2]因此,在这个定义下,铌、钼、钽、钨和铼是难熔金属。[3]在更广泛的定义下,所有熔点超过2123 K(1850 °C)的金属都是难熔金属,这样额外多了九个元素:钛、钒、铬、锆、铪、钌、铑、锇和铱。至于锝和极度不稳定的超重元素(上图中位于铹之后的元素,如𬬻、𬭊、𬭳、𬭛等无法在自然界发现)尽管符合难熔金属的定义范畴,但因其具有放射性,所以从来都不被认为是难熔金属,其中锝的熔点已经确认为2430K(2157°C),而𬬻的预测熔点为2400K(2100°C)。[4]
性质
[编辑]名称 | 铌 | 钼 | 钽 | 钨 | 铼 |
---|---|---|---|---|---|
溶点 | 2750 K (2477 °C) | 2896 K (2623 °C) | 3290 K (3017 °C) | 3695 K (3422 °C) | 3459 K (3186 °C) |
沸点 | 5017 K (4744 °C) | 4912 K (4639 °C) | 5731 K (5458 °C) | 5828 K (5555 °C) | 5869 K (5596 °C) |
密度 | 8.57 g·cm−3 | 10.28 g·cm−3 | 16.69 g·cm−3 | 19.25 g·cm−3 | 21.02 g·cm−3 |
杨氏模量 | 105 GPa | 329 GPa | 186 GPa | 411 GPa | 463 GPa |
维氏硬度 | 1320 MPa | 1530 MPa | 873 MPa | 3430 MPa | 2450 MPa |
相关条目
[编辑]参考资料
[编辑]- Levitin, Valim. High Temperature Strain of Metals and Alloys: Physical Fundamentals. WILEY-VCH. 2006. ISBN 978-3-527-31338-9.
- Brunner, T. Chemical and structural analyses of aerosol and fly-ash particles from fixed-bed biomass combustion plants by electron microscopy. 1st World Conference on Biomass for Energy and Industry: proceedings of the conference held in Sevilla, Spain, 5–9 June 2000 (London: James & James Ltd). 2000. ISBN 1-902916-15-8.
- Spink, Donald. Reactive Metals. Zirconium, Hafnium, and Titanium. Industrial & Engineering Chemistry. 1961, 53 (2): 97–104. doi:10.1021/ie50614a019.
- Hayes, Earl. Chromium and Vanadium. Industrial & Engineering Chemistry. 1961, 53 (2): 105–107. doi:10.1021/ie50614a020.
- ^ International Journal of Refractory Metals and Hard Materials. Elsevier. [2010-02-07]. (原始内容存档于2012-06-28).
- ^ Bauccio, Michael; American Society for Metals. Refractory metals. ASM metals reference book. ASM International. 1993: 120–122. ISBN 19939780871704788 请检查
|isbn=
值 (帮助). - ^ Metals, Behavior Of; Wilson, J. W. General Behaviour of Refractory Metals. Behavior and Properties of Refractory Metals. 1965-06-01: 1–28. ISBN 9780804701624.
- ^ Davis, Joseph R. Alloying: understanding the basics. 2001: 308–333 [2018-08-29]. ISBN 978-0-87170-744-4. (原始内容存档于2021-06-10).
|
|